Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
LIANGLIANG TIAN1,* , FEI WANG2
Dendritic Fe0.6Co0.4 alloy was synthesized by low temperature hydrothermal method under strong alkaline condition. Morphology, composition, structure, magnetic property and microwave absorbing property of the Fe0.6Co0.4 alloy were characterized by scanning electron microscopy (SEM), energy diffraction spectrum (EDS), X-ray diffraction (XRD), vibrating sample magnetometer (VSM) and vector network analyzer, respectively. XRD pattern reveals that the alloy shows bcc structure. The saturation magnetization, coercivity and residual magnetization is 212.39 emu/g, 56.0 Oe and 9.1 emu/g, respectively. The microwave absorbing property demonstrates that the minimum RL of the Fe0.6Co0.4 alloy is -14.08 dB at 3.1 GHz with a thickness 6.5 mm..
Dendritic, FeCo alloy, Microwave absorbing property, Permittivity, Permeability.
LIANGLIANG TIAN, FEI WANG, Synthesis and microwave absorbing property of the dendritic Fe0.6Co0.4 alloy, Optoelectronics and Advanced Materials - Rapid Communications, 7, 9-10, September-October 2013, pp.688-691 (2013).
Submitted at: Nov. 20, 2012
Accepted at: Sept. 18, 2013
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.