Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
CHUAN-JUN YUE1,* , LI-PING GU1, YANG SU1, SHAO-PING ZHU1
A Cu/MgO composite was prepared through wet mixing method with modified Raney Cu with MgO. The texture of the Cu/MgO composite was characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), and Brunauer Emm ett Teller (BET). The hydrogen adsorption and acid base properties of the composite were tested by Hydrogen Temperature Programmed Desorption (H2-TPD), CO2-TPD and NH3-TPD. Results showed that MgO was well dispersed within the pores of Raney Cu, and the co ntact interface of Cu and MgO was enhanced based on the large specific surface area of Raney Cu. A new phase of Cu MgO was formed, and the surface properties of Raney Cu were modified..
Composite, Cu/MgO, Raney Cu Wet mixing method, Surface properties.
CHUAN-JUN YUE, LI-PING GU, YANG SU, SHAO-PING ZHU, Synthesis and characterization of Cu/MgO with controllable interface based on Raney Cu by wet-mixing method, Optoelectronics and Advanced Materials - Rapid Communications, 8, 9-10, September-October 2014, pp.854-857 (2014).
Submitted at: June 20, 2013
Accepted at: Sept. 11, 2014
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.