Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
SHIRLEY PALISOC1, MICHELLE NATIVIDAD1,* , FRUMENCIO CO1, KEVIN KAW1
Nafion thin films were fabricated using the spin coating method. Hexaammineruthenium(III) [Ru(NH3)6]3+ was used as the redox mediator and was incorporated in the film. The amount of [Ru(NH3)6]3+ was varied and three different solvents were used. The morphology of the films was investigated and the film thickness was measured using scanning electron microscopy (SEM). The effects of varying the amount of the redox mediator and the solvent type on the viscosity of the coating solution, film thickness and morphology were investigated. The electrochemical properties of the fabricated films were studied using cyclic voltammetry..
Nafion, Hexaaminoruthenium(III), Spin coating, Modified electrode.
SHIRLEY PALISOC, MICHELLE NATIVIDAD, FRUMENCIO CO, KEVIN KAW, Morphological, thickness and electrochemical analyses of spin-coated [Ru(NH3)6]3+/Nafion films, Optoelectronics and Advanced Materials - Rapid Communications, 9, 7-8, July-August 2015, pp.1010-1013 (2015).
Submitted at: March 17, 2015
Accepted at: June 24, 2015
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.