Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
SERKAN ISLAK1,*
ZrO2/Al2O3 coatings with different amounts of Al2O3 were fabricated on the AISI 304 stainless steel surface using plasma spray process. Phase composition and microstructure of the coatings were characterised using X-ray diffraction and scanning electron microscopy. Lamellae and porous microstructure were obtained in the coatings. In addition, a small amount of unmelted particles, partially melted, and fully melted regions in microstructure of coatings were observed. With the increasing addition of Al2O3, a decrease in the pores was determined. The results indicated that the as-prepared ZrO2/Al2O3 based coatings were mainly composed of ZrO2, Al0.52Zr0.48O1.74, ZrTiO4, Al0.18Zr0.82O1.91, Al2O3, Al2Zr3, Al3Ti and Ti2O3 phases. The microhardness of the coating was as high as 1136 HV0.2, which was 4-5 times of the substrate..
Plasma spray, ZrO2, Al2O3, Microstructure.
SERKAN ISLAK, Effect of alumina addition on the microstructure properties of plasma-sprayed zirconia-alumina coatings, Optoelectronics and Advanced Materials - Rapid Communications, 7, 7-8, July-August 2013, pp.585-589 (2013).
Submitted at: Oct. 6, 2012
Accepted at: July 11, 2013
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.