Our site saves small pieces of text information (cookies) on your device in order to deliver better content and for statistical purposes. You can disable the usage of cookies by changing the settings of your browser. By browsing our site without changing the browser settings you grant us permission to store that information on your device.
DINESH SINGH RANA1,*
Thermally stimulated depolarization current (TSDC) measurement technique have been used to investigate the dielectric relaxation processes in 75 MeV Oxygen swift heavy ion (SHI) irradiated Polyvinylidene fluoride (PVDF). The films of 20 μm thickness were irradiated with 75 MeV Oxygen-ion at different fluence: 1.0×1010 (1.0E+10), 1.0×1011 (1.0E+11), 5.63×1011 (5.63E+11), and 5.68×1012 (5.68E+12) ions/cm2. Thermally stimulated depolarization (TSD) current measurements were carried out in the temperature range 30 –165 0C at different polarization temperature (Tp) and polarization field (Ep). The heating rate (2 ºC/min) and polarization time (1 h.) have been kept constant in all TSDC measurements. TSDC characteristics of 75 MeV Oxygen-ion irradiated PVDF show a well defined current maxima (termed as β-peak) around the polarization temperature (Tp) in the temperature region 70-118 0C. The TSDC spectra of high Tp poled samples also show a current maximum around 120 0C (termed as α-peak). The β-peak is attributed to the dipolar relaxation process. The α-peak has been ascribed to the space charge polarization process due to the formation of new deep traps and in some cases notably those corresponding to low values of Ep and Tp, The number of peaks actually appearing in these spectra and their location, height and sharpness are governed by depolarization parameters (Tp, Ep). The activation energy and pre-exponential factors corresponding to β-peak and α-peak were also estimated at different polarization temperature (Tp) and polarization field (Ep)..
PVDF, TSDC, SHI, Activation energy (U), Pre-exponential factor (τ0).
DINESH SINGH RANA, Dielectric relaxation processes studies in oxygen- swift heavy ion irradiated Polyvinylidene fluoride (PVDF) thin film using TSDC measurement technique, Optoelectronics and Advanced Materials - Rapid Communications, 6, 11-12, November-December 2012, pp.1139-1145 (2012).
Submitted at: July 15, 2012
Accepted at: Oct. 30, 2012
Optoelectronics and Advanced Materials - Rapid Communications
(2022): 0.5 - 2022 Journal Citation Reports (Clarivate Analytics, 2023)
Active accounts were imported to the new platform and assigned a random password by default. In order to access your account you need to access the login page and go through the Lost Password dialog (involves the system sending you an email with instructions) in order to reset your password. This step is necessary as passwords are kept in hashed form and the new platform uses modern hashing algorithms incompatible with the previous ones.